Hydrogen embrittlement is definitely some thing to be considered, when using electrolysis, as it can cause rapid crack formation and failure of a component.
That being said, it is predominantly the case for high strength steels, low grades are not so susceptible to embrittlement.
I would not use electrolysis for something like the U bolts that holds an axel to the springs, leaf springs or tow hook etc.
The effects of hydrogen embrittlement can be mitigated by heat treating the steel after the electrolysis to drive the hydrogen out.